1850mpa Bead Stringing Wire , 1.65mm Breaking Force

Name: 1850mpa Bead Stringing Wire , 1.65mm Breaking Force
Brand: Zhangjiagang City Shengda Steel Wire Rope Co., Ltd.
Rating: 4.9 (35 reviews)

Get Latest Price

Send Inquiry

Model No. :
Brand Name :

10yrs

Jiangsu, China

Other

Visit The Store

Zhangjiagang City Shengda Steel Wire Rope Co., Ltd.

VISIT THE STORE

You might also like

5.0% Break Elongation 38 Torsion Smooth Coating Bead Stringing Wire For Vehicles 1.60mm

5.0% Break Elongation 1870mpa Tensile Strength Bead Stringing Wire For Motorcycles 1.55mm

1900mpa Breaking Force Bead Stringing Wire For Automobiles 6.0% Break Elongation 1.65mm

Uniform Coating 2100mpa Tensile Strength Bead Stringing Wire For Motorcycles 1.60mmht

0.27g/kg Bronze Coated 500mm/3m Straightness Uniform Smooth Bead Stringing Wire 1.55mmht

Wholesale Quality 1870mpa Tensile Strength Bead Stringing Wire For Motorcycles 1.55mm

6.0% Break Elongation 1.65mm Dia. Bead Stringing Wire For Planes 2150mpa Breaking Force

1.55mm Dia. 1870mpa Tensile Strength Bead Stringing Wire Bead Wire Or Motorcycles

1870mpa Tensile Strength Bead Stringing Wire Tires Rims For Motorcycles With 1.55mm Dia.

98.3% Cu 87.6% Yield Ratio Bead Stringing Wire For Planes 2150mpa Breaking Force 1.65mmht

Product description

1850Mpa Bead Stringing Wire , 1.65mm Breaking force

Specifications:

BEAD WIRE

Diameter(mm): 1.63-1.67

Breaking force (Mpa): 2050-2150

Elongation at break(%): 5.0-6.0

Description	BEAD WIRE	Reference	GB/T14450- 2008	Diameter	Φ 1.65mmHT
Item		Standard		Result
Diameter(mm)		1.65± 0.02		1.63-1.67
Breaking force (Mpa)		≥2050		2050-2150
Elongation at break(%)		≥5.0		5.0-6.0
Yield ratio(%)		≥85		85.4-87.6
Torsion(360°/100d)		≥25		29-35
Bronze coated(g/kg)		0.20-0.40		0.32-0.36
Sn (%)		0.3-3.0		1.7
Cu(%)		≥97		98.3
Surface Quality		Coating Smooth and uniform		conform

Description:

Bead wire for tire rim is widely applied to the manufacturing of various tires rims for automobiles, motorcycles, planes as well as other vehicles.It’s the pivotal material of tire, which can strengthen the tire and is considered an important raw material for the tyre manufacturing business.

Bead wire, its cross section is circular, wire attached to the surface of plating layer, the lap steel carbon content for the 0.80%-0.85%, when the bead wire diameter is 1.50mm, the diameter of the bead wire breaking force is greater than or equal to 3700N, the elongation in4%-7%, flexor strength ratio in 90% - 97% between. Using the improved lap steel strength and fatigue strength, the total strength of the same tire bead wire, can reduce the dosage, the weight of the tire is reduced, reduce the rolling resistance of tire, save energy, and reduce the tire production cost; has high flexion strength ratio, can reduce wire the creep, prolong the life of tires.