Product description
Nickel 201 wiremesh – UNS N02201 Nickel 200 wiremesh – UNS N02200 Commercially pure Nickel 201 with similar properties to Alloy 200 but with a lower carbon content to prevent embrittlement by inter-granular carbon at elevated temperatures. Nickel 201 is the low carbon version of Nickel 200. It is preferred to Nickel 200 for applications involving exposure to temperatures above 600°F. With low base hardness and lower work-hardening rate, it is particularly suited for cold forming. Mesh: 5mesh -200mesh
Chemical Composition(%):
| Ni | Mn | C | Si | Fe | Cu | S |
Max | | 0.35 | 0.02 | 0.35 | 0.40 | 0.25 | 0.01 |
Min | 99.0 | | | | | | |
Physical Properties
Density | 8.9 g/cm3 |
Specific Heat | 440 J/kg K |
Electrical Resistivity | 8.5 micro ohms cm |
Curie Temperature | 358°C |
Melting Range | 1435-1445°C |
Thermal Expansion | (106K) 14.3 (20-300°C) |
Mechanical Properties:
Ultimate Tensile | ≥50KSi (≥345MPa) |
Yield Strength (0.2% OS) | ≥10KSi (≥70MPa) |
Elong | ≥40 |
Applications: 1. Manufacture and handling of sodium hydroxide, particularly at temperature above 300C. 2. Production of viscose rayon. Manufacture of soap. 3. Alanine hydrochloride production and in the chlorination of aliphatic hydrocarbons such as benzene, methane and ethane. 4. Manufacture of vinyl chloride monomer. 5. Reactors and vessels in which fluorine is generated and reacted with hydrocarbons.